PC LEXAN FL930 resin 耐酸碱摄像机

沙伯基础 聚碳酸酯 LEXAN  FL930 resin技术参数
性能项目 试验条件 测试方法 测试数据
比重 ——2 ASTMD792 1.13 g/cm3
比重 —— ASTMD792 1.25 g/cm3
MoldingShrinkage-Flow(6.40mm)
InternalMethod 0.50to0.70 %
吸水率(24hr)
ASTMD570 0.16 %
吸水率(平衡,23°C)
ASTMD570 0.35 %
室外适用性
UL746C f2
Foam-Physical3
InternalMethod 10 %
TensileModulus(6.40mm)
ASTMD638 2450 MPa
TensileStrength(Yield,6.35mm)
ASTMD638 50.3 MPa
伸长率(断裂,6.35mm)
ASTMD638 6.2 %
FlexuralModulus(6.40mm)
ASTMD790 2790 MPa
FlexuralStrength(Yield,6.40mm)
ASTMD790 89.6 MPa
Foam-Mechanical3
InternalMethod 10 %
悬壁梁缺口冲击强度(23°C)
ASTMD4812 750 J/m
落锤冲击(23°C)
InternalMethod 51.5 J
Foam-Impact3
InternalMethod 10 %
载荷下热变形温度(0.45MPa,未退火,6.40mm)
ASTMD648 138 °C
载荷下热变形温度(1.8MPa,未退火,6.40mm)
ASTMD648 127 °C
线形热膨胀系数-流动(-40到95°C)
ASTME831 5.0E-5 cm/cm/°C
比热
ASTMC351 1170 J/kg/°C
导热系数
ASTMC177 0.15 W/m/K
RTIElec
UL746 80.0 °C
RTIImp
UL746 80.0 °C
RTIStr
UL746 80.0 °C
Foam-Thermal3
InternalMethod 10 %
表面电阻率
ASTMD257 >1.1E+17 ohms
体积电阻率
ASTMD257 2.5E+17 ohmscm
介电常数 100Hz ASTMD150 2.22
介电常数 1MHz ASTMD150 2.12
耗散因数 100Hz ASTMD150 1.2E-3
耗散因数 1MHz ASTMD150 6.1E-3
耐电弧性4
ASTMD495 PLC7
相比耐漏电起痕指数(CTI)
UL746 PLC4
高电弧燃烧指数(HAI)
UL746 PLC4
高电压电弧起痕速率(HVTR)
UL746 PLC4
热丝引燃(HWI)
UL746 PLC1
Foam-Electrical3
InternalMethod 20 %
UL阻燃等级(6.0mm)
UL94 V-0
Foam-FlameClassMinimumDensity
InternalMethod 710 kg/m3

PC 原料相关属性（部分）
沙伯基础  PC  LEXAN FL930 resin
PC 日本帝人 Multilon  DN-7720D 填料、矿物填料、工业应用、商务设备
PC 美国RTP 306 TFE 20 注塑
PC 美国RTP RTP 300 MG 30 TFE 15
PC 沙伯基础 LEXAN  XHT3143 resin
PC 美国RTP RTP 2585 填料、碳纤维增强材料、30%填料按重量
PC 日本帝人 Multilon  TN-3616Q 阻燃性、防止持续性带电、注射成型、通用、电气元件
PC 美国RTP RTP 302 TFE 10 填料、玻璃纤维增强材料、15%填料按重量
PC 美国RTP 305 TFE 15 SI 2 注塑
PC 美国RTP 300 AR 15 TFE 15 SI 颗粒料
PC 美国RTP RTP 301 TFE 15 填料、玻璃纤维增强材料、10%填料按重量
其他相关产品
POM 德国赫斯特 9021TF 注塑
PBT 美国RTP RTP 1000 TFE 15 Z 润滑,注射成型
PP 利安德巴塞尔 EKC 170N 矿物填料,尺寸稳定性良好,良好的刚性,共聚物,良好的抗撞击性,抗紫外线性能良好,流动性高,耐刮擦性,气味低到无,韧性良好 汽车领域的应用,汽车内部零件
LDPE 沙伯基础 SABIC  LDPE HP0823J
SBR乳液 韩国锦湖 Kumho SBR 1502G
TPE 美国吉力士 V 1555A-E0285 性能特点,低压缩***变形率,耐臭氧性,高耐热性。用途,管道密封。
PA66 美国RTP EMI 260.5 H 注塑
HDPE 三井化学 2100GP 其它 适合滚塑制品
PPA 美国RTP 4007 HI 注塑
PP 埃克森美孚 7031E2 常温下抗冲性能好,尺寸稳定 电线外套,折皱型材
PE 美国路博润 Stat-Rite  S-102
PP 利安德巴塞尔 PDC1284 均聚物,刚性良好,抗静电性。应用于薄壁部件。
TPO 韩国LG化学 Lupol  HM2300 填料,矿物填料,30%填料按重量。 电气/电子应用领域
PP 沙特sabic 6604-5 注塑 用于汽车
TPV 埃克森美孚 121-65B200 其它

TYPICAL PROPERTIES (1)
MECHANICAL Value Unit Standard
FOAM - MECHANICAL 6.4 mm Wt Reduction 10 % -
Tensile Stress, yield, 6.35 mm 730 kgf/cm2 ASTM D 638
Tensile Strain, break, 6.35 mm 3 % ASTM D 638
Tensile Modulus, 6.4 mm 70600 kgf/cm2 ASTM D 638
Flexural Stress, yield, 6.4 mm 1300 kgf/cm2 ASTM D 790
Flexural Modulus, 6.4 mm 70300 kgf/cm2 ASTM D 790
IMPACT Value Unit Standard
FOAM - IMPACT 6.4 mm Wt Reduction 10 % -
Izod Impact, unnotched, 23°C 49 cm-kgf/cm ASTM D 4812
Falling Dart Impact, 23°C 414 cm-kgf SABIC Method
THERMAL Value Unit Standard
FOAM - THERMAL 6.4mm Wt Reduction 10 % -
HDT, 0.45 MPa, 6.4 mm, unannealed 143 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed 138 °C ASTM D 648
CTE, -40°C to 95°C, flow 2.16E-05 1/°C ASTM E 831
Specific Heat 1.04 J/g-°C ASTM C 351
Thermal Conductivity 0.16 W/m-°C ASTM C 177
Relative Temp Index, Elec 110 °C UL 746B
Relative Temp Index, Mech w/impact 110 °C UL 746B
Relative Temp Index, Mech w/o impact 110 °C UL 746B
PHYSICAL Value Unit Standard
FOAM - PHYSICAL 6.4mm Wt Reduction 10 % -
Specific Gravity 1.43 - ASTM D 792
Specific Gravity, foam molded 1.29 - ASTM D 792
Water Absorption, 24 hours 0.12 % ASTM D 570
Water Absorption, equilibrium, 23C 0.26 % ASTM D 570
Mold Shrinkage, flow, 6.4 mm (5) 0.2 - 0.4 % SABIC Method
ELECTRICAL Value Unit Standard
FOAM - ELECTRICAL 6.4 mm Wt Reduction 20 % -
Volume Resistivity 2.4E+17 Ohm-cm ASTM D 257
Surface Resistivity >1.1E+17 Ohm ASTM D 257
Relative Permittivity, 100 Hz 2.7 - ASTM D 150
Relative Permittivity, 1 MHz 2.61 - ASTM D 150
Dissipation Factor, 100 Hz 0.0034 - ASTM D 150
Dissipation Factor, 1 MHz 0.0075 - ASTM D 150
Arc Resistance, Tungsten {PLC} 7 PLC Code ASTM D 495
Hot Wire Ignition {PLC) 1 PLC Code UL 746A
High Voltage Arc Track Rate {PLC} 3 PLC Code UL 746A
High Ampere Arc Ign, surface {PLC} 4 PLC Code UL 746A
Comparative Tracking Index (UL) {PLC} 4 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
FOAM - Flame Class Minimum Density 0.9 g/cm3 -
UL Recognized, 94V-0 Flame Class Rating (3) 5.99 mm UL 94
UL Recognized, 94-5VA Rating (3) 5.99 mm UL 94
Oxygen Index (LOI) 40.4 % ASTM D 2863

品牌代理经销批发的PA66/PP/PC/POM/PET/ABS、PBT/PEI/PPS等塑胶原料*消费者市场，在消费者当中享有较高的地位，公司与多家零售商和代理商建立了长期稳定的合作关系。公司经销的PA66/PP/PC/POM/PET/ABS、PBT/PEI/PPS等品种齐全、价格合理。公司实力雄厚，重信用、守合同、保证产品质量，以多品种经营特色和薄利多销的原则，赢得了广大客户的信任