技术参数

性能项目 试验条件[状态] 测试方法 测试数据 数据单位
物理性能 比重
ASTMD792,ISO1183 1.19 g/cm3
熔流率(熔体流动速率)(300°C/1.2kg)
ASTMD1238 10 g/10min
溶化体积流率(MVR)(300°C/1.2kg)
ISO1133 9.50 cm3/10min
收缩率 流动:3.20mm 内部方法 0.40到0.80 %
横向流动:3.20mm 内部方法 0.40到0.80 %
吸水率 饱和,23°C ISO62 0.12 %
平衡,23°C,50%RH ISO62 0.093 %
硬度 洛氏硬度(L计秤)
ISO2039-2 90
机械性能 --1
ASTMD638 2220 MPa
--
ISO527-2/1 2350 MPa
屈服2
ASTMD638 58.0 MPa
屈服
ISO527-2/50 57.9 MPa
断裂3
ASTMD638 64.1 MPa
断裂
ISO527-2/50 61.5 MPa
屈服4
ASTMD638 5.8 %
屈服
ISO527-2/50 5.5 %
断裂5
ASTMD638 130 %
断裂
ISO527-2/50 120 %
50.0mm跨距6
ASTMD790 2220 MPa
--7
ISO178 2150 MPa
--8
ISO178 90.2 MPa
屈服,50.0mm跨距9
ASTMD790 94.3 MPa
冲击性能 简支梁缺口冲击强度10 -30°C ISO179/1eA 50 kJ/m2
23°C ISO179/1eA 70 kJ/m2
简支梁无缺口冲击强度11 -30°C ISO179/1eU 无断裂
23°C ISO179/1eU 无断裂
无缺口伊佐德冲击强度14 -30°C ISO180/1U 无断裂
23°C ISO180/1U 无断裂
装有测量仪表的落镖冲击 -30°C,TotalEnergy ASTMD3763 85.0 J
23°C,TotalEnergy ASTMD3763 82.4 J
热性能 1.8MPa,未退火,3.20mm
ASTMD648 124 °C
1.8MPa,未退火,64.0mm跨距15
ISO75-2/Af 119 °C
--
ASTMD1525,ISO306/B501116 141 °C

ISO306/B120 142 °C
BallPressureTest(125°C)
IEC60695-10-2 Pass
流动:-40到95°C
ASTME831 7.2E-5 cm/cm/°C
流动:23到80°C
ISO11359-2 7.2E-5 cm/cm/°C
横向:-40到95°C
ASTME831 7.9E-5 cm/cm/°C
横向:23到80°C
ISO11359-2 7.9E-5 cm/cm/°C
RTIElec
UL746 130 °C
RTI
UL746 130 °C
电气性能 表面电阻率
ASTMD257 >1.0E+15 ohms
体积电阻率
ASTMD257 >1.0E+15 ohms·cm
可燃性 UL阻燃等级(2.50mm)
UL94 V-2
灼热丝易燃指数(3.00mm)
IEC60695-2-12 960 °C
热灯丝点火温度 0.800mm IEC60695-2-13 825 °C
3.00mm IEC60695-2-13 825 °C
光学性能 透射率(2540μm)
ASTMD1003 82.0 %
雾度(2540μm)
ASTMD1003 3.0 %

  是五大泛用工程塑胶中具有良好透明性的塑胶，可见光透率高达90%以上，加上材质轻、隔热性能比无机玻璃高25%，抗冲击强度是无机玻璃250 倍，特别适用于玻璃及板材，聚碳酸酯板材在建筑方面需用量占PC总需求量40%以上。聚碳酸酯板材可制成的各种复杂的板材，可用于建筑物大面积屋顶、走廊、楼梯护栏、阳台围墙等，具有安全可靠，坚固耐用及外观美丽等优点。由于PC的冲击强度、硬度、耐候性和耐热性，汽车应用领域包括汽车的离合器系统、仪表板、照明灯具、内外部嵌板和轮胎盖子及汽车玻璃等。而聚碳酸酯的光学特性及其独特的耐冲击性、耐候性以及量轻、强度高等特性，越来越多应用在汽车灯罩，近年美国、日本、欧洲汽车制造厂也开始以聚碳酸酯作为灯罩的材料。 PC生产厂商GE公司和拜耳公司也联手研发汽车车窗玻璃用聚碳酸酯，期许车窗玻璃全部用聚碳酸酯代替。

  最初只用于飞机座舱罩和挡风玻璃，随着航太技术发展，对飞机和航空器各零件品质要求不断提高，使得聚碳酸酯在该领域的应用也日渐增加。1架747飞机所用的聚碳酸酯零件约2公吨，太空船上也是由数百种玻璃纤维补强的聚碳酸酯零件组成。在食品包装领域，PC主要用于饮用水瓶及奶瓶家用食品容器等，但是由于原料双酚A 列为危险化学物质，因此聚碳酸酯应用在食品包装领域将受到严峻的挑战，聚碳酸酯将来是否应用在食品包装领域仍是一个未知数。

属性

加工方式

资料

 视觉搜索

 曲线数据

购买地点

单位: SI

总体  
材料状态 

已商用：当前有效

资料 1 

Technical Datasheet

UL 黄卡 2 

E121562-256637

搜索 UL 黄卡 

SABIC Innovative Plastics

供货地区 

北美洲

添加剂 

紫外线稳定剂

特性 

共聚物

可加工性，良好

快的成型周期

流动性中等

通用

延展性

用途 

电气/电子应用领域

电子显示器

汽车领域的应用

外观 

不透明

清晰/透明

 
加工方法 

注射成型

Also Available In 

Asia Pacific

Europe

 
物理性能
额定值

单位制

测试方法

密度 / 比重

1.19

g/cm3

ASTM D792, ISO 1183
熔流率（熔体流动速率） (300°C/1.2 kg)

10

g/10 min

ASTM D1238
熔融体积流量（MVR） (300°C/1.2 kg)

9.00

cm3/10min

ISO 1133
收缩率

  内部方法
流动 : 3.20 mm

0.40 到 0.80

%

 
横向流动 : 3.20 mm

0.40 到 0.80

%

 
吸水率

  ISO 62
饱和, 23°C

0.12

%

 
平衡, 23°C, 50% RH

0.090

%

 
硬度
额定值

单位制

测试方法

洛氏硬度 (L 计秤)

89

ISO 2039-2
机械性能
额定值

单位制

测试方法

拉伸模量

   
-- 3

2210

MPa

ASTM D638
--

2350

MPa

ISO 527-2/1
抗张强度

   
屈服 4

58.0

MPa

ASTM D638
屈服

57.0

MPa

ISO 527-2/50
断裂 4

64.0

MPa

ASTM D638
断裂

61.0

MPa

ISO 527-2/50
伸长率

   
屈服 4

5.8

%

ASTM D638
屈服

5.5

%

ISO 527-2/50
断裂 4

130

%

ASTM D638
断裂

120

%

ISO 527-2/50
弯曲模量

   
50.0 mm 跨距 5

2210

MPa

ASTM D790
-- 6

2150

MPa

ISO 178
弯曲应力

   
-- 6, 7

90.0

MPa

ISO 178
屈服, 50.0 mm 跨距 5

94.0

MPa

ASTM D790
冲击性能
额定值

单位制

测试方法

简支梁缺口冲击强度 8

  ISO 179/1eA
-30°C

50

kJ/m2

 
23°C

70

kJ/m2

 
简支梁无缺口冲击强度 8

  ISO 179/1eU
-30°C

无断裂

 
23°C

无断裂

 
悬壁梁缺口冲击强度

   
-30°C

800

J/m

ASTM D256
23°C

890

J/m

ASTM D256
-30°C 9

45

kJ/m2

ISO 180/1A
23°C 9

65

kJ/m2

ISO 180/1A
无缺口伊佐德冲击强度 9

  ISO 180/1U
-30°C

无断裂

 
23°C

无断裂

 
装有测量仪表的落镖冲击

  ASTM D3763
-30°C, Total Energy

85.0

J

 
23°C, Total Energy

82.0

J

 
热性能
额定值

单位制

测试方法

载荷下热变形温度

   
1.8 MPa, 未退火, 3.20 mm

124

°C

ASTM D648
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10

118

°C

ISO 75-2/Af
维卡软化温度

   
--

141

°C

ASTM D1525 11, ISO 306/B50 11
--

142

°C

ISO 306/B120
Ball Pressure Test (123 到 127°C)

通过

IEC 60695-10-2
线形热膨胀系数

   
流动 : -40 到 95°C

7.2E-5

cm/cm/°C

ASTM E831
流动 : 23 到 80°C

7.2E-5

cm/cm/°C

ISO 11359-2
横向 : -40 到 95°C

7.9E-5

cm/cm/°C

ASTM E831
横向 : 23 到 80°C

7.9E-5

cm/cm/°C

ISO 11359-2
RTI Elec

130

°C

UL 746
RTI

130

°C

UL 746
电气性能
额定值

单位制

测试方法

表面电阻率

> 1.0E 15

ohms

ASTM D257
体积电阻率

> 1.0E 15

ohms·cm

ASTM D257
可燃性
额定值

单位制

测试方法

UL 阻燃等级 (2.5 mm)

V-2

UL 94
灼热丝易燃指数 (3.0 mm)

960

°C

IEC 60695-2-12
热灯丝点火温度

  IEC 60695-2-13
0.8 mm

825

°C

 
3.0 mm

825

°C

 
光学性能
额定值

单位制

测试方法

透射率 (2540 μm)

82.0

%

ASTM D1003
雾度 (2540 μm)

3.0

%

ASTM D1003
注射
额定值

单位制

干燥温度

沙伯基础创新塑料（Sabic）的商品名，Lexan PC聚碳酸酯由双酚A制造,为聚碳酸脂这高分子材料,具有 的耐热性能、良好的透明度和较高的耐冲击强度等物理机械性能。聚碳酸酯无色透明，耐热，抗冲击，阻燃BI级，在普通使用温度内都有良好的机械性能。同性能接近聚甲基丙烯酸甲酯相比，聚碳酸酯的耐冲击性能好，折射率高，加工性能好，不需要添加剂就具有UL94 V-0级阻燃性能。PC工程塑料的三大应用领域是玻璃装配业、汽车工业和电子、电器工业，其次还有工业机械零件、光盘、包装、计算机等办公室设备、医疗及保健、薄膜、休闲和防护器材等。
聚碳酸酯是日常常见的一种材料。由于其无色透明和优异的抗冲击性，日常常见的应用有光碟，眼镜片，水瓶，防弹玻璃，护目镜、银行防子弹之玻璃、车头灯等等、动物笼子宠物笼子等。
聚碳酸酯PC也是笔记本电脑外壳采用的材料的一种，它的原料是石油，经聚酯切片工厂加工后就成了聚酯切片颗粒物，再经塑料厂加工就成了成品，从实用的角度，其散热性能也比ABS塑料较好，热量分散比较均匀运用这种材料比较显着的就是FUJITSU了，在很多型号中都是用这种材料，而且是全外壳都采用这种材料。不管从表面还是从触摸的感觉上，PC-GF材料感觉都像是金属。如果笔记本电脑内没有标识的话，单从外表面看不仔细去观察，可能会以为是合金物。
聚碳酸酯还被用来制作登月太空人的头盔面罩。苹果公司的iPod音乐播放器和ibook笔记本电脑外壳也使用聚碳酸酯制作。
由于它的清晰和韧性，食物贮存货的生产者和采购员喜欢聚碳酸酯纤维。当与矽土玻璃比较聚碳酸酯纤维如同轻量级和高度不易碎。聚碳酸酯纤维多用于一次性塑料水瓶和重用塑料水瓶。
化学性质聚碳酸酯耐弱酸,耐中性油。
聚碳酸酯不耐紫外光,不耐强碱。物理性质比重:1.18-1.20克/立方厘米 成型收缩率:0.5-0.8% 成型温度：230-320℃ 干燥条件：100-110，4-5小时 可在 -60~120℃下长期使用。
物料性能 冲击强度高，尺寸稳定性好，无色透明，着色性好，电绝缘性、耐腐蚀性、耐磨性好，但自润滑性差，有应力开裂倾向，高温易水解，与其它树脂相溶性差。 适于制作仪表小零件、绝缘透明件和耐冲击零件
PC EXL1414H LEXAN--市场应用聚碳酸酯的应用开发是向高复合、高功能、**化、系列化方向发展，目前已推出了光盘、汽车、办公设备、箱体、包装、照明、薄膜等多种产品各自**的品级牌号。
用于建材行业

PC的改性:并用溴类阻燃剂和三氧化二锑，可制成阻燃级PC。
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 590 kgf/cm2 ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 650 kgf/cm2 ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5.8 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 131.4 % ASTM D 638
Tensile Modulus, 50 mm/min 22500 kgf/cm2 ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 960 kgf/cm2 ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 22500 kgf/cm2 ASTM D 790
Tensile Stress, yield, 50 mm/min 57 MPa ISO 527
Tensile Stress, break, 50 mm/min 61 MPa ISO 527
Tensile Strain, yield, 50 mm/min 5.5 % ISO 527
Tensile Strain, break, 50 mm/min 124.9 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2150 MPa ISO 178
Hardness, Rockwell L 89 - ISO 2039-2
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 90 cm-kgf/cm ASTM D 256
Izod Impact, notched, -30°C 81 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy, 23°C 840 cm-kgf ASTM D 3763
Instrumented Impact Total Energy, -30°C 866 cm-kgf ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m2 ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m2 ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 65 kJ/m2 ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 55 kJ/m2 ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 70 kJ/m2 ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 60 kJ/m2 ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m2 ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m2 ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate A/50 141 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 124 °C ASTM D 648
CTE, -40°C to 95°C, flow 7.15E-05 1/°C ASTM E 831
CTE, -40°C to 95°C, xflow 7.93E-05 1/°C ASTM E 831
CTE, 23°C to 80°C, flow 7.15E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 7.93E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C pass - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 141 °C ISO 306
Vicat Softening Temp, Rate B/120 142 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 118 °C ISO 75/Af
Relative Temp Index, Elec 130 °C UL 746B
Relative Temp Index, Mech w/o impact 130 °C UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.19 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5) 0.4 - 0.8 % SABIC Method
Mold Shrinkage, xflow, 3.2 mm (5) 0.4 - 0.8 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 10 g/10 min ASTM D 1238
Density 1.19 g/cm3 ISO 1183
Water Absorption, (23°C/sat) 0.12 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.09 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 9 cm3/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission, 2.54 mm 82 % ASTM D 1003
Haze, 2.54 mm 3 % ASTM D 1003
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm ASTM D 257
Surface Resistivity >1.E+15 Ohm ASTM D 257
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-2 Flame Class Rating (3) 2.5 mm UL 94
Glow Wire Flammability Index 960°C, passes at 3 mm IEC 60695-2-12
Glow Wire Ignitability Temperature, 0.8 mm 825 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm 825 °C IEC 60695-2-13
Source GMD, last updated:2004/09/15
Processing
LEXAN EXL1810T resin聚碳酸酯SABIC Innovative Plastics产品说明：LEXAN EXL1810T聚碳酸酯（PC）硅氧烷共聚物树脂是一种透明注塑级树脂。与标准PC树脂相比，该树脂具有低温（0°C）延展性、极高的流动特性和优异的加工性能，并具有更短的IM循环时间。LEXAN EXL1810T树脂是一种通用产品，有透明和不透明两种颜色可供选择，是广泛应用的理想选择。

  
Parameter
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 215 - 295 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm

产品说明 LEXAN EXL1463T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with medium flow characteristics, improved release and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1463T resin is an improved release general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications. 总体 材料状态 已商用：当前有效供货地区 北美洲特性 共聚物可加工性，良好延展性快的成型周期流动性中等脱模性能良好通用用途 通用外观 不透明清晰/透明 加工方法 注射成型

应商建立长期的合作关系， 的一手货源，保证质量的可靠性与价格的合理性，且我司拥有自己的原料改性厂，可根据客户产品的实际需求进行各种增强改性，达到客户所需的理想效果，使客户以 的投入获取 的回报。
以下是关于PC聚碳酸酯塑胶粒的一些简单介绍，的价格及详细资料欢迎来电咨询或索取！
PC最明显的特性就是其具有较高的抗冲击性，且拥有 的韧性、电气性能优异、能够在-40~180摄氏度的温度范围内使用，且收缩小尺寸稳定性佳。无味，透明度佳，属于无定型热塑性塑料，其主要特点如下；
1. 突出的物理性能，PC材料在刚性和韧性上能够达到 的均衡，尺寸稳定收缩小，具有相当好的耐蠕变性，耐低温性优异，即使在零下40度仍能保持良好的冲击强度。
2. 高耐热性，PC原料注塑时分解温度在300度以上，玻璃化转变温度140~150摄氏度，普通的PC材料能够长期在125摄氏度的使用环境下工作，像拜耳APEC特殊耐热级PC料，更可高达180度的热变形温度，被广泛用于汽车前后灯罩，同时PC材料又具有极好的耐低温特性，完全催化温度在零下100度，像SABIC公司研发的超韧PC树脂，极限使用温度为-50~120摄氏度，大大提高了此种材料的适用范围。
3. 良好的透明度：PC的光学性能优异，可用作照明灯具材料，通用级PC的透射率为88%，光学级PC材料的透光率可达到91%，比如日本出光LC1500，LC1700等，可用作手机导光板等高透明制件，但是PC制品的透明度越高，材料的抗冲击性越差，而且对400nm以下的紫外光的透过能力很弱。
4. 耐候性；PC原料与其他的工程塑料相比，其户外适用性优异，具有优良的抗紫外线性，且这种材料具有很强的耐老化性特点，不会因为长时间的使用而使制品变黄发脆等。尤其是PC板材可在户外使用5年以上而性能基本保持不变。
Lexan EXL1112T--PC可通过与其他塑料的合金改性进一步完善其综合性特点，如在汽车领域，早在多年前PC/PBT合金就已经得到广泛的应用，如汽车门外嵌板，他能弥补PC不能够喷漆烘烤的严格要求，还有如汽车保险杠，尤其是在仪表盘的应用最为常见，另外包括汽车灯罩，车窗等，因为这种材料具有良好的抗冲击效果，优异的表面外观，无味，质轻，今后作为汽车内饰件，这种材料在汽车领域将得到更为广泛的开发与应用。
国内已有许多工程公司已经具备设计建设大型聚酯工业化生产装置的能力，国内机械加工行业近些年来也取得了突飞猛进的发展，加工能力和加工精度已经能满足酯交换法PC生产工艺的需要。通过我们考察，除主要聚合反应器外，酯交换法Pc连续化生产装置中的其他设备都可用借鉴和借用国内聚酯生产装置的技术和设备。现在国内20万t／a聚酯生产装置的设计和加工已经基本实现了国产化，因此酯交换法PC生产装置基本可以实现国产化。
我国PC合成技术经过半个世纪的发展，仍未形成自己的具有工业规模的生产装置，整体水平较低，远远落后于发达国家，目前我国PC市场广阔，开发建设大型PC生产装置的各个方面的条件已经形成，因此，利用我国自己的科研成果和工程技术建立万吨级非光酯交换法PC生产装置，争取在未来该领域的竞争中占有一席之地，完全符合国家的产业政策，对缓解我国目前PC十分尖锐的供需矛盾，打破外国公司对我国PC生产技术的封锁和产品、价格的垄断，有着十分重要意义和良好的发展前景。

主要性能
a、机械性能：强度高、耐疲劳性、尺寸稳定、蠕变也小（高温条件下也极少有变化）；
b、耐热老化性：增强后的UL温度指数达120~140℃（户外长期老化性也很好）；
c、耐溶剂性：无应力开裂；
d、对水稳定性：遇水易分解（高温、高湿环境下使用需谨慎）；
e、电气性能：
1、绝缘性能：优良（潮湿、高温也能保持电性能稳定,是制造电子、电气零件的理想材料）；
2、介电系数：3.0-3.2；
3、耐电弧性：120s；
f、成型加工性：普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程塑料要求低。在加工薄壁制件时，仅需几秒钟，对大部件也只要40-60s即可。

公司供应沙伯沙伯基础 PC牌号如下（部分）,了解更多牌号，请电话联系


产品

性能特点

LEXAN EXL1413T resin

共聚物; 可加工性良好; 延展性; 快的成型周期; 流动性中等; 通用

LEXAN EXL1414 resin

共聚物; 可加工性良好; 快的成型周期; 流动性中等; 通用; 脱模性能良好; 延展性

LEXAN EXL1414H resin

共聚物; 可加工性良好; 延展性; 水解稳定; 流动性中等

LEXAN EXL1414T resin

共聚物; 可加工性良好; 延展性; 快的成型周期; 流动性中等; 通用

LEXAN EXL1433T resin

共聚物; 可加工性良好; 延展性; 快的成型周期; 流动性中等; 通用

LEXAN EXL1434 resin

共聚物; 可加工性良好; 快的成型周期; 流动性中等; 脱模性能良好; 通用

LEXAN EXL1434T resin

共聚物; 可加工性良好; 延展性; 快的成型周期; 流动性中等; 通用

LEXAN EXL1443T resin

共聚物; 可加工性良好; 延展性; 快的成型周期; 流动性中等; 食品接触的合规性

LEXAN EXL1444 resin

共聚物; 可加工性良好; 延展性; 流动性中等; 脱模性能良好; 食品接触的合规性

LEXAN EXL1463T resin

共聚物; 可加工性良好; 延展性; 快的成型周期; 流动性中等; 脱模性能良好; 通用

LEXAN EXL1494T resin

共聚物; 可加工性良好; 延展性; 快的成型周期; 流动性中等; 脱模性能良好; 食品接触的合规性

LEXAN EXL1810T resin

共聚物; 可加工性良好; 延展性; 快的成型周期; 流动性高

LEXAN EXL1890T resin

共聚物; 可加工性良好; 延展性; 快的成型周期; 流动性高; 脱模性能良好; 食品接触的合规性